{"id":806,"date":"2013-11-22T10:11:02","date_gmt":"2013-11-22T16:11:02","guid":{"rendered":"https:\/\/advancedplatingtech.com\/?p=806"},"modified":"2024-11-25T08:50:51","modified_gmt":"2024-11-25T14:50:51","slug":"passivation-process-for-engineering-medical-industries","status":"publish","type":"post","link":"https:\/\/advancedplatingtech.com\/blog\/passivation-process-for-engineering-medical-industries\/","title":{"rendered":"Passivation of Stainless Steel for Critical Applications"},"content":{"rendered":"

By S Patel<\/em><\/p>\n

\"passivated<\/a>Passivation is a critical processing step in the manufacturing of stainless steel components to enhance the corrosion\u00a0resistance and make stainless steel parts truly \u201cstain-less.\u201d Proper passivation of stainless steel components can make the difference between satisfactory field performance and premature corrosion failures.\u00a0 If performed improperly, the passivation process can actually attack and etch the stainless surface or induce corrosion. Passivation is often misunderstood to be a scale removal or bright dipping process when in fact it is fully removed from either of these processes.\u00a0 The information within the blog serves to detail some of the key principles of passivation of stainless steel<\/a> offered by Advanced Plating Technologies.<\/p>\n

There are two primary functions of the passivation process as follows:<\/b><\/p>\n

    \n
  1. Removal of free iron particle\/residue from stainless steel parts which may have deposited during machining, grinding, forming or stamping operations as well as from shop dirt and\/or debris. The need for passivation arises when parts are fabricated, either by cold forming or machining where contaminants such as shop dirt or iron particles from cutting tools\/fixtures may be transferred to part surface.\u00a0 If not removed, the free iron particles can corrode very rapidly giving the appearance that the stainless steel itself is rusting.<\/li>\n
  2. To develop a protective passive oxide film on the surface of the components. This passive layer is 100,000 times thinner than a human hair but forms a physical barrier to corrosion or attack of the stainless steel material beneath.\u00a0 It is this passive oxide barrier that the term \u201cpassivation\u201d stems from.<\/li>\n<\/ol>\n

    \u00a0 There are two primary passivation categories as follows:<\/b><\/p>\n

      \n
    1. Nitric Acid Passivation:<\/b>\u00a0 Nitric acid passivation processes are offered either with or without sodium dichromate at various temperatures, chemistry concentrations and exposure times\/ranges.\u00a0 The specific process is a function of the specific stainless steel material grade.<\/li>\n
    2. Citric Acid Passivation:<\/b> Citric Acid passivation processes are offered at various temperature & pH ranges.\u00a0 The specific processes are also a function of the stainless steel material grade.<\/li>\n<\/ol>\n

      Cleaning and Descaling Prior to Passivation<\/h2>\n

      \"passivated<\/a>The material grade and as-formed surface condition are the most important factors in properly specifying a cleaning & passivation protocol. \u00a0Most commonly as-formed stainless steel components have light oil on the surface.\u00a0 This film needs to be thoroughly removed by soaking parts in caustic cleaning solution or organic degreasing solvent. \u00a0The acid chemistry used for passivation process is not capable of removing oil or grease from the surface of the parts.\u00a0 If not removed, the acid will not evenly wet the surface resulting in inconsistent processing.\u00a0 In addition, residual oil on the surface will react with acidic chemistry and create oxygen bubbles which further interfere with the passivation process.<\/p>\n

      Some passivation components, such as precipitation-hardened grades (e.g. 17-4, 15-5 or 17-7), are heat treated after machining\/forming but prior to the passivation process.\u00a0 Heat treatments are performed to achieve final surface hardness that these grades offer.\u00a0 However, these processes often impart an oxide or discoloration scale\/iris on the surface even when performed in an \u201cinert\u201d environment.\u00a0 These films must be removed prior to passivation operations by means of acid descaling or mechanical methods such as blasting.\u00a0 The passivation chemistry is not capable of removing heat treatment oxide films and parts.\u00a0 If this is not performed, the heat treatment oxide will impair the ability of the passivation acid to reach the surface of the stainless steel and will prevent proper passivation.<\/p>\n

      Passivation of Stainless Steel \u2013 Proper Processing and Bath Maintenance<\/div>\n

      \"Passivated<\/a>Contamination in either nitric or citric acid chemistry can be detrimental to the passivation process.\u00a0 This is especially true of chloride which can lead to flash-attack or etching of the surface of the parts being passivated. Instead of achieving the desired oxide film with a clean and corrosion-resisting surface, flash attack will produce a heavy etched or darkened surface.\u00a0\u00a0 A common chloride contamination limit is no greater than 60 mg\/litter in either citric or nitric acid passivation chemistries.\u00a0 It is important to note that some low nickel alloys such as Martensitic 400-series grades can mildly etch during a normal passivation process.\u00a0 This mild etching of the surface is not indicative of flash attack and is not representative of process contamination.<\/p>\n

      Free-machining (e.g. 303, 416, 440F), Ferritic and Martensitic grades of stainless steel (400 series) often exhibit improved passivation if processed with an AAA (Alkaline-Acid-Alkaline) passivation process. This process was originally developed by Carpenter Technology (www.cartech.com<\/a>) for passivation of free machining stainless grades. It was discovered during standard passivation processes, the phosphorus or sulfur added to free machining alloys to improve machinability would etch from the surface leaving a micro voids on the surface.\u00a0 These voids act as micro capillaries that can trap nitric & citric acid during the passivation process. If the trapped acid is not neutralized it can result in an acid attack on the surface and accelerate corrosion. The AAA process has the ability of neutralizing acid from the surface of the parts greatly improving the passivation and corrosion resistance of the passivated components.\u00a0 As such, the AAA process is highly recommended for all free machining grades as well as Ferritic and Martensitic grades of stainless steel.\u00a0 More information is available regarding the AAA method of passivation within the white papers<\/a> of our technical library.<\/p>\n

      Citric acid passivation is an alternative process to nitric that is commonly used in the medical and food processing industries. Since nitric acid passivation utilizes nitric acid and in some cases sodium dichromate, a source of hexavalent chromium ions, citric acid is sometimes preferred in applications where food processing or human contact is a design consideration.<\/p>\n

      Advanced Plating Technologies offers all methods of passivation including nitric, citric and AAA methods.\u00a0 Specifications including QQ-P-35 and ASTM A967 provide a table reference of recommended passivation methods as a function of material grade.\u00a0 Federal specifications<\/a> are available within the technical library of this site.\u00a0 In addition, a member of the Advanced Plating Technologies technical sales or engineering group can provide recommended best practices based upon material grade, design concerns and the as-received condition of the parts.<\/p>\n

      Passivation of Stainless Steel – Testing of Passivated Parts<\/b>\u00a0\u00a0 \u00a0<\/b><\/p>\n

      Passivated parts can be tested via several methods as described in ASTM A380 or ASTM A967 but not all tests are suitable for all grades of stainless steel. The test methods include the following methods:<\/p>\n

        \n
      1. Water immersion test<\/li>\n
      2. High humidity test<\/li>\n
      3. Salt spray test<\/li>\n
      4. Copper Sulfate Test<\/li>\n
      5. Potassium Ferricyanide-Nitric Acid Test<\/li>\n<\/ol>\n

        \"small<\/a>Among the above tests copper sulfate is the most common & frequently used in industries. The copper sulfate is a favorable test due to the fact that it is nondestructive and quickly performed on a wide range of test samples. However, the copper sulfate test is not recommended for all alloys and can yield a false positive test on Martensitic or low chromium Ferritic grades of stainless steel.<\/p>\n

        If you would like additional information on test methods, passivation of stainless steel<\/a> or passivation of medical alloys<\/a> including titanium, MP35N or Elgiloy, you can contact<\/a> a member of our technical sales team.<\/p>\n","protected":false},"excerpt":{"rendered":"

        By S Patel Passivation is a critical processing step in the manufacturing of stainless steel components to enhance the corrosion\u00a0resistance…<\/p>\n","protected":false},"author":1,"featured_media":7532,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"_acf_changed":false,"jetpack_post_was_ever_published":false,"_jetpack_newsletter_access":"","_jetpack_dont_email_post_to_subs":false,"_jetpack_newsletter_tier_id":0,"_jetpack_memberships_contains_paywalled_content":false,"_jetpack_memberships_contains_paid_content":false,"footnotes":"","jetpack_publicize_message":"","jetpack_publicize_feature_enabled":true,"jetpack_social_post_already_shared":false,"jetpack_social_options":{"image_generator_settings":{"template":"highway","default_image_id":0,"font":"","enabled":false},"version":2},"_wpas_customize_per_network":false},"categories":[34],"tags":[],"class_list":["post-806","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-passivation"],"acf":[],"jetpack_publicize_connections":[],"jetpack_featured_media_url":"https:\/\/advancedplatingtech.com\/wp-content\/uploads\/2019\/07\/APT-Blog-1.png","jetpack_sharing_enabled":true,"jetpack_shortlink":"https:\/\/wp.me\/p7G6ce-d0","_links":{"self":[{"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/posts\/806","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/comments?post=806"}],"version-history":[{"count":0,"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/posts\/806\/revisions"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/media\/7532"}],"wp:attachment":[{"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/media?parent=806"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/categories?post=806"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/advancedplatingtech.com\/wp-json\/wp\/v2\/tags?post=806"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}